Affiliations: Department of Metallurgical and Materials Engineering, Istanbul University, Istanbul, Turkey
Note: [] Address for correspondence: Ilven Mutlu, Department of Metallurgical and Materials Engineering, Istanbul University, Istanbul, Turkey. Tel.: +905365718461; Fax: +902124737003; E-mail: [email protected].
Abstract: In this study, biocompatibility of 17-4 PH stainless steel foam for biomedical implant applications was investigated. 17-4 PH stainless steel foams having porosities in the range of 40–82% with an average pore size of around 600 μm were produced by space holder-sintering technique. Sintered foams were precipitation hardened for times of 1–6 h at temperatures between 450–570°C. Compressive yield strength and Young's modulus of aged stainless steel foams were observed to vary between 80–130 MPa and 0.73–1.54 GPa, respectively. Pore morphology, pore size and the mechanical properties of the 17-4 PH stainless steel foams were close to cancellous bone. In vitro evaluations of cytotoxicity of the foams were investigated by XTT and MTT assays and showed sufficient biocompatibility. Surface roughness parameters of the stainless steel foams were also determined to characterize the foams.
Keywords: Metal foam, implant, 17-4 PH stainless steel, biocompatibility, cytotoxicity