Abstract: Ultra high molecular weight polyethylene (UHMWPE) has been used in artificial joints for a few decades, and wear of UHMWPE has been one of the main problems. Though many other materials have been tested over the years, the best clinical results are still achieved with UHMWPE. This makes the study of UHMWPE, especially in relation to artificial joints, very important. Frequently, more severe wear can be observed in artificial knee joints than in artificial hip joints especially when the flaking-like wear occurs. This flaking-like wear can lead to significant destruction of the artificial knee joint. Macroscopically, artificial knee joints have combinational movements of rolling and sliding in order to simulate the motion of the normal knee joint. The components of motion are separated to make study easier. Fatigue tests of UHMWPE under the rolling contact condition were performed in this study. Three ceramic spheres were rolled over the UHMWPE specimen using 37°C distilled water as a lubricant. The UHMWPE specimen was observed by the scanning acoustic tomography, microscopy, and SEM. Some subsurface defects could be observed by SAT even before experiments. Although the apparent wear is not observed on the surface, there was an increase in the number of observable subsurface cracks in the UHMWPE specimen. This shows that cracks occur under the surface after a 107 rolling contact loading, which is very close to the cyclic loading and unloading with very little friction compared to the sliding contact.