Bonding of an opaque resin to silane-treated porcelain

Issue title: Frontiers in Biomedical Engineering and Biotechnology – Proceedings of the 3rd International Conference on Biomedical Engineering and Biotechnology, 25–28 September 2014, Beijing, China

Article type: Research Article

Authors: Li, Rui | Sun, Ying Chun | Wang, Chen | Gao, Ping;

Affiliations: Department of Prosthodontics, Stomatological Hospital, Tianjin Medical University, Tianjin 300070, China

Note: [] Corresponding author: Ping Gao, Department of Prosthodontics, Stomatological Hospital, Tianjin Medical University, Tianjin 300070, China. Tel.: +86 022 23332034; Fax:+86 022 23332036; E-mail: [email protected].

Keywords: Opaque resin, silane, porcelain, bond strength

DOI: 10.3233/BME-141022

Journal: Bio-Medical Materials and Engineering, vol. 24, no. 6, pp. 2117-2125, 2014

Published: 2014
Get PDF open access

Abstract

The repair of a fractured porcelain surface with a resin composite was investigated. The effects of applying an opaque resin to porcelain surfaces, which were silanated by a ceramic primer from a repair kit or by an experimental silane coupling agent, were studied. The porcelain surfaces were silanated for 10 sec and 60 min. Three types of adherents were evaluated: opaque resin with light irradiation (OWL), opaque resin without light irradiation (ONL), and no opaque resin (NAO). The shear bond strengths of the resins to the porcelain surfaces were measured before and after thermocycling. The maximum shear bond strength (6.7 MPa) after thermocycling was observed when the silanating period of the ceramic primer was 60 min. The opaque resin had no effect on the bond strength. Moreover, the bond strength obtained with the experimental silane coupling agent was found to be reduced by only 2 MPa, even after thermocycling.