Abstract: Results concerning the influence of Mo addition and thermal
treatment on the Hall effect and magnetoresistance of
Co_{68.25-x}Fe_{4.5}Si_{12.25}B_{15}Mo_x
(x=1; 2) ribbons in the amorphous, nanocrystallized and
crystallized states are reported. The value of the Hall resistivity of the
samples increases continuously with applied magnetic field up to about 7 kOe
and 13 kOe for
Co_{67.25}Fe_{4.5}Si_{12.25}B_{15}Mo_1and
Co_{66.25}Fe_{4.5}Si_{12.25}B_{15}Mo_2
alloys, respectively and then it approaches saturation. For
Co_{67.25}Fe_{4.5}Si_{12.25}B_{15}Mo_1ribbons
the ferromagnetic anisotropic resistivity (FAR) values are 2.78 ×
10^{-4}, 2.60 × 106^{-4}and 2.84 ×
10^{-4} for amorphous, nanocrystalline and crystalline states,
respectively. The FAR values of
Co_{66.25}Fe_{4.5}Si_{12.25}B_{15}Mo_2
ribbons are 1.35 × 10^{-4}, 1.78 × 10^{-4} and
18 × 10^{-4}for amorphous, nanocrystalline and
crystalline states, respectively.