Affiliations: Department of Conservative Dentistry and Endodontics, SRM Institute of Science and Technology, SRM Dental College, Chennai, India
Correspondence:
[*]
Corresponding author: Sampath Vidhya, Department of Conservative Dentistry and Endodontics, SRM Institute of Science and Technology, SRM Dental College, Chennai, India. E-mail: [email protected].
Abstract: BACKGROUND: Undesirable effects of tooth bleaching can alter the biomechanical properties of enamel. OBJECTIVE: To determine the influence of strontium fluorophosphate bioactive glass (Sr-FPG) on color, microhardness and surface roughness of enamel bleached with 35% hydrogen peroxide. METHODS: The labial enamel of 36 extracted intact human anterior teeth were divided into 3 groups (n= 12), group 1 (HP): bleaching with 35% hydrogen peroxide only, group 2 (Sr-HP): bleaching with Sr-FPG incorporated 35% hydrogen peroxide and group 3 (HP-SrFPG): bleaching with 35% hydrogen peroxide followed by remineralization with Sr-FPG. Four consecutive eight-minute applications of the bleaching gel were done twice in all the groups. Color change (ΔE), microhardness and surface roughness were evaluated at baseline, post-bleaching and post-remineralization using spectrophotometer, Vickers hardness tester and profilometric analysis respectively. RESULTS: The mean ΔE among the groups was statistically similar (p> 0.05). Bleaching with HP significantly reduced microhardness (p< 0.05), whereas bleaching with Sr-HP and HP-SrFPG did not (p> 0.05). Post-bleaching microhardness in Sr-HP was significantly higher than HP-SrFPG (p< 0.05). An increased surface roughness was seen in Sr-HP bleached samples (p< 0.05). CONCLUSION: The addition of Sr-FPG to hydrogen peroxide significantly improved enamel microhardness than its use post-bleaching. An increase in surface roughness was seen post-bleaching with HP and Sr-HP.